LPSCl Li6PS5Cl White Solid Electrolyte Sulfide Powder for Solid-State lithium ion Battery Raw Material |
|
|
|
Batch No.
|
SC20230312
|
|
|
|
theoretical density
|
2 g/cm3
|
|
|
|
Chemical formula
|
Li6PS5Cl
|
|
|
|
ITEM
|
Standard
|
Test method/equipment
|
|
|
Appearance (powder)
|
Grey white, uniform, without foreign objects
|
/
|
|
|
Appearance (cold pressed forming)
|
Grey
|
/
|
|
|
Appearance (heat treated to porcelain)
|
Black
|
/
|
|
|
SEM Morphology
|
Granularity 2-50μm
|
Hitachi S4800
|
|
|
Main crystal phase |
Li-Argyrodite Li7PS6,Structure of sulfur silver germanium ore(RefFacile Synthesis toward the Optimal Structure-Conductivity
Characteristics of the Argyrodite Li6PS5Cl Solid-State ElectrolyteDOI= 10.1021/acsami.8b07476)RefPDF2004 #34-0688 |
Brook D8 Advance |
|
|
secondary crystalline phase
|
Unable to detect Li2S raw material phase and other impurities
|
|
|
|
Ionic conductivity (powder not pressurized)
|
~8 mS/cm@27°C |
Metrohm Autolab ECI10
|
|
|
Ionic conductivity
(Powder cold pressing) |
~12 mS/cm@27°C The test results of carbon indium lithium electrode are slightly different
|
Metrohm Autolab ECI10
|
|
|
Electronic conductivity
(Powder cold pressing) |
<1×10 −8 S/cm@27°C |
Metrohm Autolab AUT87627
|
|
|
Electronic conductivity
(Ceramic) |
<1×10 −7 S/cm@27
|
Metrohm Autolab AUT87627
|
|
|
Conductivity activation energy
(Powder cold pressing) |
0.275 eV (26.6 kJ/mol) (25~85 °C) |
Solartron 1470E+1455A
|
|