PVDF powder for Lithium Battery coating adhesive resin PVDF
PRODUCT FEATURE
PVDF copolymer has medium viscosity and is suitable for extrusion and for solution processing in lithium batteries applications.
SPECIFICATIONS
General
|
Material Status
|
Commercial: active |
| Availability |
Africa; Middle East; Europe; Asia Pacific; North America; South America |
| Features |
Copolymer; Good flexibility; Medium viscosity |
| Process Method |
Extrusion; solution processing |
Physical
|
Item
|
Typical Value Unit | Test Method |
|
Specific Gravity |
1.75 to 1.80 g/cm3 |
ASTM D792 |
|
Melt Mass-Flow Rate(MFR)(230/5.0kg) |
3.0 to 9.0 g/10min |
ASTM D1238 |
|
Water Absorption(23,24hr) |
<0.040% |
ASTM D570 |
Mechanical
|
Item
|
Typical Value Unit | Test Method |
|
Tensile Modulus1(23,2.0mm) |
360 to 480 Mpa |
ASTM D638 |
|
Tensile Strength2 Yield, 23,2.00mm Break, 23,2.00mm |
15.0-18.0 Mpa 20.0-40.0 Mpa |
ASTM D638 |
|
Tensile Elongation2 Yield, 23,2.00mm Break, 23,2.00mm |
12 to 15% 600 to 750% |
ASTM D638 |
Thermal
|
Item
|
Typical Value Unit | Test Method |
|
Glass Transition Temperature |
-40.0 |
ASTM D4065 |
|
Melting Temperature |
130-136 |
ASTM D3418 |
|
Peak Crystallization Temperature(DSC) |
89.0 to 93.0 |
ASTM D3418 |
|
Crystallization Heat |
20.0 to 24.0 j/g |
ASTM D3417 |
|
Heat of Fusion |
20.0 to 24.0 j/g |
ASTM D3417 |
Electrical
|
Item
|
Typical Value Unit | Test Method |
|
Surface Resistivity |
>1.0E+14 ohm |
ASTM D257 |
|
Volume Resistivity |
>1.0E+14 ohm'cm |
ASTM D257 |
NOTES:
Typical properties: these are not to be construed as specifications
1 type IV, 1.0mm/min