| Customization: | Available |
|---|---|
| Type: | Electrode |
| Product Name: | Ceramic Battery Separator |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| No. | Test Term | Unit | Inspection value | |
| 1 | Thickness | micron | 20.0±2.0 | |
| 2 | Surface density | g/m2 | 17.0±2.0 | |
| 3 | Ceramic layer Surface density | g/m2 | 8.0±1.5 | |
| 4 | Gas permeability | Sec/100ml | 250±40 | |
| 5 | Gas permeability increment | % | ≤15% | |
| 6 | Puncturing Strength | gf | ≥580 | |
| 7 | 120ºC *1h shrinking percentage | MD | % | ≤2.0 |
| 8 | TD | % | ≤1.5 | |
| 9 | Tensile strength | MD | Mpa | ≥150 |
| 10 | TD | Mpa | ≥135 | |
| 11 | Tensile Elongation |
MD | % | ≥50 |
| 12 | TD | % | ≥50 | |
| 13 | Film close temperature | ºC | ≤135 | |
| 14 | Width | mm | ||
| 15 | Length | m | ||
| 16 | Peel strength | N/m | ≥40 | |
| 17 | Static electricity | KV | ≤2.0 | |
| 18 | Water content | ppm | ≤1200 | |
| No. | Test Term | Unit | Inspection value | |
| 1 | Thickness | micron | 16.5±1.0 | |
| 2 | Surface density | g/m2 | 9.0±1.5 | |
| 3 | Porosity | % | 42±5 | |
| 4 | Gas permeability | Sec/100ml | 190±30 | |
| 5 | Puncturing Strength | N | ≥5.8 | |
| 6 | 105ºC *1h shrinking percentage | MD | % | ≤5.0 |
| 7 | TD | % | ≤3.0 | |
| 8 | Tensile strength | MD | Kgf/cm² | ≥1900 |
| 9 | TD | Kgf/cm² | ≥1800 | |
| 10 | Tensile Elongation |
MD | % | ≥50 |
| 11 | TD | % | ≥50 | |
| 12 | Film close temperature | ºC | ≤135 | |
){kind=link}